影响因子：3.1
DOI码：10.3390/met11030404
所属单位：清华大学
发表刊物：Metals
摘要：A hot rolled Al-5Mg-2Li-0.2Sc-0.12Zr alloy sheet with an initial banded microstructure was subjected to high-temperature tensile tests in the temperature range of 450–550 °C, at strain rates ranging from 3 × 10−4 to 1 × 10−2 s−1. The microstructural evolution of the present non-ideal superplastic microstructure (banded morphology) was characterized by electron back-scattered diffraction (EBSD) and transmission electron microscopy (TEM). The results show that the hot rolled non-ideal superplas...
合写作者：Yang Xiao, Kaijie Ma, Yuhan Wang, Zhipeng Liu, Zhenjie Liu, Wenjing Zhang
第一作者：Chengzhi Zhang
论文类型：期刊论文
通讯作者：Wenjing Zhang
论文编号：404
学科门类：工学
一级学科：材料科学与工程
文献类型：J
卷号：11
期号：3
页面范围：404
ISSN号：2075-4701
是否译文：否
发表时间：2021-03-01