DOI码：10.1088/0953-2048/17/4/022
所属单位：北京科技大学
发表刊物：Superconductor Science and Technology
刊物所在地：英国
摘要：Bulk MgB2 with SiO2 nanoparticles added has been synthesized using a simple solid-state reaction route. The lattice constant in the c direction increases with additive content due to a small amount of Si being doped into the lattice of the MgB2; however, T-c is almost fixed at 37.2 K. The addition Of SiO2 nanoparticles also improves the J(c)-H and H-irr-T characteristics of MgB2 when the additive content is lower than 7%. At 20 K and 1 T, J(c) for the sample with 7% additive content reaches 2.5 x 10(5) A cm(-2).
合写作者：Y. Zhao, Y. Y. Xu, L. Zhang, X. F. Sun, Y. Z. Wang, H. Zhang
第一作者：X. F. Rui
论文类型：期刊论文
通讯作者：Han Zhang
学科门类：工学
文献类型：J
卷号：17
期号：4
页面范围：689-691
ISSN号：0953-2048/1361-6668
是否译文：否
发表时间：2004-04-01
发布期刊链接：https://iopscience.iop.org/article/10.1088/0953-2048/17/4/022